电线电缆LDPE 中石油大庆石化 2420D 注塑级
| 加工方法 | 吹塑薄膜 吹塑成型 挤出 挤出吹塑成型 |
| 比重 | 0.922 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| 薄膜厚度 - 经测试 | 35 | µm | |
| 膜刺穿力 (35 µm) | 14.1 | N | ASTM D3420 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 35 µm | 20.0 | MPa | ASTM D882 |
| TD : 断裂, 35 µm | 19.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 100 µm | 35 | % | ASTM D882 |
| TD : 断裂, 35 µm | 500 | % | ASTM D882 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 35 µm | 200 | g | ASTM D1922 |
| TD : 35 µm | 250 | g | ASTM D1922 |
| Impact Resistance, Film | 280 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 48.0 | MPa | ASTM D882 |
| TD | 62.0 | MPa | ASTM D882 |