高刚性 耐应力开裂 HDPE 泰国BPE H5604F 薄膜级
EL-Lene™ H5604F
High Density Polyethylene
SCG Chemicals Co., Ltd.
产品说明：
EL-LENE H5604F is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan.
物性信息：
| 特性 | 低速凝固晶点 防潮 刚性，高 抗撞击性，高 食品接触的合规性 |
| 用途 | 薄膜 袋子 通用 重包装袋 |
| 机构评级 | FDA 21 CFR 177.1520 |
| 形式 | 粒子 |
| 加工方法 | 吹塑薄膜 |
| 密度 | 0.956 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.040 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 (50°C, 25% Igepal, 模压成型, F50) | > 1000 | hr | ASTM D1693B |
| 可供应的薄膜厚度 | 10 to 25 µ | ||
| 割线模量 | ASTM D882 | ||
| 2% 正割, MD : 12 µm | 804 | MPa | ASTM D882 |
| 2% 正割, TD : 12 µm | 785 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| TD : 屈服, 12 µm | 24.5 | MPa | ASTM D882 |
| MD : 断裂, 12 µm | 60.8 | MPa | ASTM D882 |
| TD : 断裂, 12 µm | 30.4 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 12 µm | 240 | % | ASTM D882 |
| TD : 断裂, 12 µm | 450 | % | ASTM D882 |
| 落锤冲击 (12 µm) | 140 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 12 µm | 3.0 | g | ASTM D1922 |
| TD : 12 µm | 80 | g | ASTM D1922 |
| 脆化温度 | < -60.0 | °C | ASTM D746 |
| 维卡软化温度 | 124 | °C | ASTM D1525 |
| 熔融温度 | 131 | °C | ASTM D2117 |
| 熔体温度 | 190 到 210 | °C |
展开全文