PC 基础创新塑料(南沙) 141R-701 注塑级
| Flexural Strain at Flexural Strength (23°C) 6 | 7.1 | % | ISO 178 |
| Gas Permeation | ISO 2556 | ||
| Carbon Dioxide : 23°C, 25.4 µm | 16900 | cm³/m²/bar/24 hr | ISO 2556 |
| Carbon Dioxide : 23°C, 100.0 µm | 3800 | cm³/m²/bar/24 hr | ISO 2556 |
| Nitrogen : 23°C, 25.4 µm | 510 | cm³/m²/bar/24 hr | ISO 2556 |
| Nitrogen : 23°C, 100.0 µm | 120 | cm³/m²/bar/24 hr | ISO 2556 |
| Oxygen : 23°C, 25.4 µm | 2760 | cm³/m²/bar/24 hr | ISO 2556 |
| Oxygen : 23°C, 100.0 µm | 650 | cm³/m²/bar/24 hr | ISO 2556 |
| Application of Flame from Small Burner - Method K and F (2.00 mm) | K1, F1 | DIN 53438-1, -3 | |
| Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 | |
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Glow Wire Test | EDF HN60 E.02 | ||
| 1.50 mm | 750 | °C | EDF HN60 E.02 |
发布时间：2025-01-12
展开全文
其他新闻
- 注塑标准 级抗冲性好PC 基础创新塑料(南沙) 243R-111 阻燃级 2025-01-12
- PC 基础创新塑料(南沙) 3412R-131级抗冲性好 流动好原料 2025-01-12
- PC 基础创新塑料(南沙) 940-701 注塑级 2025-01-12
- PC 泰国科思创（拜耳） 6557 阻燃级 2025-01-12
- PC 泰国科思创（拜耳） 6555 阻燃级 2025-01-12
- PC 上海科思创（拜耳） 2805 550115 注塑级高抗冲 高流动鞋类 2025-01-12
- PC 基础创新塑料(南沙) 940NC 注塑级 2025-01-12
- PC1000R 透明 沙特基础创新塑料 注塑级 聚碳酸酯 2025-01-12
- 透明级,阻燃级PC 浙江石化 G2010-G 家电部件 2025-01-11
- PC 上海帝人 GN-3620H 阻燃增强级 2025-01-11