LLDPE 沙特埃克森美孚 LL 6201XR注塑级 高流动 包装 容器
| 密度 | 0.926 g/cc | 0.0335 lb/in³ | ExxonMobil method |
| ESCR 10% Igepal® | 6.0 hour | 6.0 hour | ASTM D1693B |
| 熔体流动速率 | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 抗张强度(屈服) | 10.3 MPa | 1500 psi | ASTM D638 |
| 伸长率 (断裂) | 100 % | 100 % | ASTM D638 |
| 屈服伸长率 | 20 % | 20 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 283 MPa | 41000 psi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 42.0 kJ/m² | 20.0 ft-lb/in² | ISO 180/1A |
| 熔融温度 | <= 253 °C | <= 487 °F | Peak Melti |
| 密度 | 0.926 g/cc | 0.0335 lb/in³ | ExxonMobil method |
| ESCR 10% Igepal® | 6.0 hour | 6.0 hour | ASTM D1693B |
| 熔体流动速率 | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 抗张强度(屈服) | 10.3 MPa | 1500 psi | ASTM D638 |
| 伸长率 (断裂) | 100 % | 100 % | ASTM D638 |
| 屈服伸长率 | 20 % | 20 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 283 MPa | 41000 psi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 42.0 kJ/m² | 20.0 ft-lb/in² | ISO 180/1A |
| 熔融温度 | <= 253 °C | <= 487 °F | Peak Melti |
发布时间：2024-11-15
展开全文
其他新闻
- LLDPE 中石化广 州 DFDA-7144 瓶盖用料家电部件塑胶原料 2024-11-15
- 高韧性 无臭 高强度 注塑级LLDPE 中石化 M2720A 通用塑料 2024-11-15
- LLDPE 中石化广州 M2320 薄膜级 2024-11-15
- LLDPE 中石化广 州 DFDA-7042 注塑级 食品级 吹塑级 薄膜级 2024-11-15
- 坑原检测试剂盒原料LDPE韩国LG MB9500 注塑级 人工草坪 塑料花 2024-11-15
- LDPE 中石化茂名 868-000 注塑级 2024-11-15
- LDPE卡塔尔石化MG70 熔指70 高流动 薄膜级低密度 核酸裂解管专用料 2024-11-15
- LDPE 日本尤尼卡 DNDV0405R 薄膜级 透明 高流动 包装 2024-11-15
- 透明级 LDPE 中石化茂 名 2426H 薄膜级 耐高温 吹塑级 农膜 2024-11-15
- LDPE中石化茂 名 PEM1850A挤出级高流动高光泽密度聚乙烯 2024-11-15